Examinando por Autor "Baldo, Edgardo"
Mostrando 1 - 5 de 5
Resultados por página
Opciones de ordenación
- Documento de conferencia
Acceso Abierto Characterization of ASR products in a 40-year-old highway(2012) Locati, Francisco; Marfil, Silvina Andrea; Maiza, Pedro; Baldo, EdgardoThe majority of crushed aggregates utilized in Argentina come from the Sierras Pampeanas of Córdoba, (Province of Córdoba). Many of the exploited lithologies are quartz-rich and have undergone deformation processes affecting their texture and producing internal microstructures. Previous studies have shown that those characteristics make rocks potentially alkali reactive. In order to compare those results with performance of aggregates in concrete structures, an important highway that links Córdoba and Villa Carlos Paz cities was studied. Preliminary results showed that this deterioration could be interpreted as a normal aging of concrete, accelerated by humidity problems and ASR development. In this work, further studies on reaction products were carried out through a stereomicroscope, a polarized light microscope, powder XRD and SEM-EDS analyses. Calcium silicates with variable contents of sodium and potassium, associated with ettringite, were identified in fissures, mortar, in the mortar-aggregate interface and filling air voids. - Documento de conferencia
Acceso Abierto Comportamiento de rocas metamórficas con venas de pseudotaquilitas de las sierras chicas de Córdoba, frente a la reacción álcali-sílice(2008) Marfil, Silvina Andrea; Baldo, Edgardo; Batic, Oscar R.; Locati, FranciscoEn este trabajo se evalúa el comportamiento de rocas metamórficas con venas de pseudotaquilitas de la zona de Las Bateas (Quebrada del Río Suquía, Sierras Chicas de Córdoba, Argentina), frente a la reacción álcali-sílice (RAS), utilizando métodos de ensayo convencionales. Se efectuó la caracterización petrográfico-mineralógica del material, mediante estudios sobre secciones delgadas y difractometría de rayos X, identificándose material vítreo, cuarzo microcristalino y tensionado con extinción ondulante, como especies deletéreas. Se midió la expansión en barras de mortero (IRAM 1674). Se determinó la sílice disuelta según el método de ensayo químico (IRAM 1650). Se analizó el contenido de Al2O3, CaO, K2O, FeO, MgO y MnO lixiviados a la solución y su relación con la SiO2 y la expansión medida en las barras de mortero. Los estudios realizados por los métodos físicos, químicos y petrográficos son coincidentes y permiten concluir que el material estudiado es potencialmente reactivo frente a la RAS. - Artículo
Acceso Abierto Effect of ductile deformation of quartz-bearing rocks on the alkali-silica reaction(2010) Locati, Francisco; Marfil, Silvina Andrea; Baldo, EdgardoIt has been known for a long time that strained, microcrystalline or cryptocrystalline quartz-bearing aggregates may cause alkali-silica reactions in concrete. Studying the relationship between deformation processes and microstructural characteristics of rocks, the reason for this behaviour can be better understood. Orthogneisses from the metamorphic basement of the Sierra Chica, Córdoba (Argentina), which were locally and differentially deformed in ductile shear zones, were used to analyse such behaviour. Petrographic analyses, accelerated mortar bar tests (ASTM C 1260, 2005) and chemical test (ASTM C 289, 1994) were conducted. Furthermore, corrosion tests were performed on polished rock surfaces using 1 N NaOH solution. It was seen that the reactivity of the quartz-bearing mylonites increased by ~30% with respect to the non-mylonitised sample due to the increment in the strained quartz content and specially with the extended subgrain development. The mylonitised rock affected by superimposed cataclasis and the development of pseudotachylytic veins incremented its reactivity by ~97% with respect to the nonmylonitised sample due to the combined effects of subgrain formation, grain size reduction and the formation of glassy material. It was also the only sample that showed significant differences in surface corrosion confirming the high reactivity of the rock. These results agree with expansion values measured on the accelerated mortar bar test and with silica leached in the chemical test. We believe that the simultaneous use of different tools to evaluate the potential alkali reactivity of the rocks in concrete is a good strategy rather than the use of isolated tools, which could lead to confusing interpretations of the process and therefore result in erroneous decisions. - Artículo
Acceso Abierto Na2O, K2O, SiO2 and Al2O3 release from potassic and calcic–sodic feldspars into alkaline solutions(2010) Locati, Francisco; Marfil, Silvina Andrea; Baldo, Edgardo; Maiza, PedroThe potential release of elements from potassic and calcic–sodic feldspars into the concrete pore solution was evaluated by ICP-MS using 1 N NaOH and KOH solutions at 80 °C in accordance with the conditions set in the chemical test method. Materials were characterized by petrography, XRD and by XRF analysis. The influence of textural and microstructural characteristics on the leaching process was also analyzed by immersing polished plates of each mineral in 1 N NaOH at 80 °C for 7 days. Optical microscope and SEM observations indicate that microstructural characteristics, such as cleavage zones, twins, grain–grain contact and the finer and less abundant phases in perthites, play a key role in the leaching process under alkaline conditions. Na2O, K2O, SiO2 and Al2O3 are supplied by hydrolysis, although the participation of other processes cannot be ruled out. - Documento de conferencia
Acceso Abierto Tremolita Asbestiforme en mármoles de Altautina, provincia de Córdoba(2014) Locati, Francisco; Lescano, Leticia; Murra, Juan; Baldo, Edgardo; Maiza, Pedro; Marfil, Silvina AndreaLos afloramientos de mármoles en las Sierras de Córdoba (SC), están ampliamente distribuidos y su composición varía desde extremos dolomíticos a cálcicos, con predominio de los primeros. El porcentaje de minerales accesorios es igualmente variable siendo tremolita, flogopita, diópsido y forsterita los más comunes. Por lo general yacen en forma de bancos tabulares o lenticulares frecuentemente plegados, asociados a rocas para y ortoderivadas del basamento (gneises, esquistos, migmatitas, anfibolitas y rocas ultramáficas). Al oeste de las sierras, en la zona de Altautina, son mayoritariamente dolomíticos, de grano medio a fino y con un residuo insoluble que varía entre 2% y 25%, siendo la tremolita el principal mineral accesorio junto a otros silicatos como talco y serpentina (Sfragulla et al. 1999). Este mineral, de hábito prismático, por lo general presenta formas planares a fibrosas de gran desarrollo, y puede observarse diseminado en la masa carbonática, como relleno de venas o en planos de discontinuidad. En algunos sectores, estos anfíboles se agrupan en haces de fibras >; 5 μm de largo, <3 μm de diámetro y relación largo/ancho >3, lo que los califica como minerales del grupo de los asbestos (ej: OSHA 1992). Este término no representa a un solo mineral sino que describe a un grupo de silicatos hidratados de magnesio, fibrosos y muy flexibles. Presentan además, resistencia química, eléctrica y térmica por lo que su uso comercial se ha extendido mundialmente (Veblen y Wylie 1993). Si bien la explotación e importación de asbestos ha sido prohibida a nivel nacional en consonancia con otros países del mundo (Rodríguez 2004), la determinación y caracterización de anfíboles asbestiformes resulta de sumo interés ya que éstos podrían ser liberados durante las tareas de explotación de los mármoles del sector, o degradados por procesos de meteorización en escombreras expuestas durante largos períodos de tiempo.