Aplicación del Método Acelerado CAMBT para evaluar la reactividad alcalina de agregados

cic.isFulltexttruees
cic.isPeerReviewedtruees
cic.lugarDesarrolloLaboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica es
cic.versioninfo:eu-repo/semantics/submittedVersiones
dc.date.accessioned2014-12-15T11:53:30Z
dc.date.available2014-12-15T11:53:30Z
dc.identifier.urihttps://digital.cic.gba.gob.ar/handle/11746/130
dc.titleAplicación del Método Acelerado CAMBT para evaluar la reactividad alcalina de agregadoses
dc.typeArtículoes
dcterms.abstractPara evaluar la reactividad alcalina de los agregados, en Argentina se aplican el análisis petrográfico (IRAM 1649 / ASTM C295), el acelerado de la barra de mortero (IRAM 1674 / ASTM C1260) y el del prisma de hormigón (IRAM 1700 / ASTM C1293). Dado que en algunos casos los resultados de métodos diferentes no concordaban entre sí, se recurrió a un método de ensayo acelerado, de origen chino (CAMBT). Conceptualmente se asemeja al método ASTM C1260 con diferencias en la granulometría y en las proporciones de los agregados, el tipo de cemento y el tamaño de las probetas. El estacionamiento se realiza en NaOH 1N a 80ºC y el límite de aceptación máximo para la expansión es de 0,093% a 16 días. Se muestran los resultados de 6 agregados, tres granitos, una sienita cuarcífera, una ortocuarcita y un basalto. Los resultados obtenidos son congruentes con las diferentes mineralogías y los estudios previos o el comportamiento en obras de hormigón existentes que utilizaron algunos de estos agregados.es
dcterms.abstractIn order to evaluate the alkaline reactivity of aggregates, in Argentina are applied the petrographic analysis (IRAM 1649 / ASTM C295), accelerated mortar bar test (IRAM 1674 / ASTM C1260) and concrete prism test (IRAM 1700 / ASTM C1293 .) Since in some cases the results of different methods did not agree with each other, a Chinese accelerated mortar bar test (CAMBT) was tested. Conceptually it is similar to ASTM C1260 with differences in the granulometry and proportions of aggregates, cement type and specimens size. The storage is done in 1N NaOH at 80°C and the maximum limit of acceptance for the expansion is 0.093% at 16 days. The results of six aggregates, three granites, a quartz syenite, an ortoquartzite and a basalt are shown. The obtained results are consistent with the different mineralogies and previous studies, or its behaviour in several concrete structures made by using some of this aggregates.en
dcterms.alternativeApplicability of Accelerated Mortar Bar Test (CAMBT) in the evaluation of alkaline reactivity of aggregatesen
dcterms.creator.authorFalcone, Darío Danieles
dcterms.creator.authorBatic, Oscar R.es
dcterms.extent6 p.es
dcterms.isPartOf.issuenº 2es
dcterms.isPartOf.seriesCiencia y Tecnología de los Materialeses
dcterms.issued2012
dcterms.languageEspañoles
dcterms.licenseAttribution 4.0 International (BY 4.0)es
dcterms.subjectreacción álcali-sílicees
dcterms.subjectensayos acelerados CAMBTes
dcterms.subjectdiferentes mineralogíases
dcterms.subjectAlkali-silica reactionen
dcterms.subjectaccelerated tests CAMBTen
dcterms.subjectdifferent mineralogiesen
dcterms.subject.materiaHormigónes
Archivos
Paquete original
Mostrando1 - 1 de 1
Imagen en miniatura
Nombre:
05-Falcone.pdf
Tamaño:
751.14 KB
Formato:
Adobe Portable Document Format
Descripción:
Documento completo